SiC Grinding bead

SiC Grinding bead

Short Description:

silicon carbide bead items units SiC density g/cm3 3.12 absorbing rate % 0 CTE 106/k 3 Young’s elastic modulus Gpa 440 Parking ratio / 0.17 hardness(Hv) MPa 2800 bending strength(RT) MPa 390 bending strength(700℃) MPa 380 compressive strength(RT) MPa 1800 breaking tenacity MPa·m1/2 3.9 heat conductivity(RT) W/m·k 120 electrical resistivity(RT) Ω·mm2/m >103 maximum ser...


  • Port: Jiangxi
  • Product Detail

    Product Tags

    silicon carbide bead

    items

    units

    SiC

    density

    g/cm3

    3.12

    absorbing rate

    %

    0

    CTE

    106/k

    3

    Young’s elastic modulus

    Gpa

    440

    Parking ratio

    /

    0.17

    hardness(Hv)

    MPa

    2800

    bending strength(RT)

    MPa

    390

    bending strength(700℃)

    MPa

    380

    compressive strength(RT)

    MPa

    1800

    breaking tenacity

    MPa·m1/2

    3.9

    heat conductivity(RT)

    W/m·k

    120

    electrical resistivity(RT)

    Ω·mm2/m

    >103

    maximum service temperature( non-load)

    1550

    acid and alkali resistance

    /

    strong


  • Previous:
  • Next:

  • Related Products

    Contact Us

    • Jiangxi Sanxin New Materials Co.,Ltd.
    • Phone: 0086-799-6779577
    • E-mail: sale@sxceramics.cn
    • Fax: +86-799-6779566
    • Whatsapp: 008615879969889

    INQUIRY FOR PRICELIST

    For inquiries about our products or pricelist, please leave your email to us and we will be in touch within 24 hours.

    Latest News

    WhatsApp Online Chat !